Description
: High build modified aluminium primer
Principal Characteristics
: Highly impermeable to water
: Good wetting properties
: Good adhesion to steel, aged conventional point substrates and shopprimed steel
: Very tolerant to dry docking conditions
: Easy to apply by airless spray
: Suitable as sealer coat for a variety of leached out antifouling types
Colours and Gloss
: Aluminium light and dark - flat
Basic data at 30 ˚C
Solid content
: approx. 43% by volume
Recommended dry film thickness
: 75µm
Theoretical spreading rate
: 5.7 m2/1 for 75µm on smooth and non absorbent surfaces
Touch dry after
: 20 minutes
Overcoating interval
: minimum 3 hours at 30 ˚C
: maximum unlimited provided surface is cleaned
Shelf life (cool and dry place)
: atleast 12 months
Flash point
: 27 ˚C
Recommended substrate conditions and temperature
: Steel blast cleaned to Sa 2 1/2 of Swedish specification
Conditions and Temperature
: Steel with approved zinc silicate shop primer; sweep blasted to SPSS-Ss
: Aged conventional coat; high pressure water cleaned to remove all contamination
: The temperature of the substrate must be atleast 3 ˚C above dew point
Instruction for use
: stir well before use
: The temperature of the point should be above 15 ˚C otherwise extra thinner may be required to obtain application viscosity
: Too much solvent results in lower sag resistance